Continuous Deposition of Buffer Layers for YBCO Coated Conductor Using Reactive Magnetron Sputtering

2007 
A reel-to-reel deposition system was set up for studying YBCO coated conductor. Continuous deposition of multi-layer CeO2/YSZ/Y2O3 buffer layers was carried out on 10mm-width biaxially textured tape of NiW using the reactive dc magnetron sputtering technique. A continuous and uniform buffer layer with good texture was presented over length. For 10–meter-long tapes, the φ-scan FWHM values of Y2O3 (222), YSZ (111), and CeO2 (111) were 7.77°, 7.68° and 7.93°, respectively. The rocking curves showed that the average FWHM values of Y2O3 (004), YSZ (002), and CeO2 (002) were 5.02°, 4.67° and 4.44°, respectively. The microstructure and interfaces of buffer layers were observed by scanning electron microscopy (SEM) and Auger electron spectrum (AES). YBCO layer was prepared by magnetron sputtering technique as well on the short samples.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    10
    References
    6
    Citations
    NaN
    KQI
    []