Sputtering of Mo and Al in D2/N2 plasma cleaning discharge

Abstract Sputtering of Mo and Al (as Be proxy) in mixed D 2 /N 2 DC glow discharge was studied in view of the first mirror performance. The composition of the working gas was varied from 100% D 2 to 100% N 2 , while keeping a total pressure of 15 Pa. The ion energies striking the sample surface were defined by its 100 V biasing negative to a floating potential. It has been obtained that the sputtering yield of Mo and Al increases gradually with N 2 concentration up to 4‒16 mol% and decreases with further N 2 addition. In contrast, the sputtering yield of Be remains unchanged up to 10 mol% of N 2 . Adding 16 mol% leads to three-fold decrease in the sputtering rate. The sputtering behavior is discussed in context of surface data analysis and mass spectroscopy of the discharge gas exhaust. Variation in reflectivity of a single crystalline Mo due to plasma exposure under similar conditions is also presented and discussed.