Microwave assisted rapid growth of flat ZnO(0001) platelets

BaksidestextThe understanding of the surfaces of materials is of crucial importance to all of us. Considering nanocrystals (NCs), that have a large surface to bulk ratio, the surfaces become even more important. In the work in this thesis ZnO NCs were studied.The fundamental properties of ZnO surfaces were studied using distributions of ZnO NCs on SiO2/Si surfaces. Annealing at 650 °C in UHV cleaned the surfaces of the ZnO NCs enough for sharp LEEM imaging and chemical characterization while no sign of de-composition was found. A flat energy band structure for the ZnO/SiO2/Si system was proposed after 650 °C. Increasing the annealing temperature to 700 °C causes a de-composition of the ZnO that induce a downward band bending on the surfaces of ZnO NCs.Flat ZnO NCs with predominantly polar surfaces were grown using a microwave assisted process. Tuning the chemistry in the growth solution the growth was restricted to only plate-shaped crystals, i.e. a very uniform growth. The surfaces of the NCs were characterized using AFM, revealing a triangular reconstruction of the ZnO(0001) surface not seen without surface treatment at ambient conditions before. Following cycles of sputtering and annealing in UHV, we observe by STM a surface reconstruction interpreted as 2x2 with 1/4 missing Zn atoms.