Mossbauer studies of nanocrystalline Fe/sub 83/B/sub 9/Nb/sub 7/Cu/sub 1/ alloy by flash annealing
1997
Melt-spun Fe/sub 83/B/sub 9/Nb/sub 7/Cu/sub 1/ alloy with ultrathin ribbon has been studied with Mossbauer spectroscopy and X-ray diffraction. The enhanced magnetic property of the flash-annealed alloy was attributed to the reduced /spl alpha/-Fe phase grain size to 6 nm and the higher effective permeability and smaller magnetic core loss at 1 MHz than conventional annealed alloys. The occupied area of the nanocrystalline phase at the optimum 773 K is about 73% whereas that for conventional annealing temperature at 893 K is about 71%. The flash annealing technique was effective in improving the high-frequency soft magnetic property of nanocrystalline Fe/sub 83/B/sub 9/Nb/sub 7/Cu/sub 1/ alloy.