Fabrication of a transversal multilayer thermoelectric generator with substituted calcium manganite

The sintering behavior and thermoelectric performance of Ca0.99Gd0.01Mn0.99W0.01O3 was studied, and a multilayer thermoelectric generator was fabricated. The addition of CuO as sintering additive was found to be effective for the reduction of the sintering temperature from 1300°C to about 1000°C – 1050°C. Dense samples were obtained after firing at 1050°C, whereas some porosity remained after firing at 1000°C. Samples sintered at reduced temperature exhibit lower electrical conductivity, whereas the Seebeck coefficient S = -150 μV/K at 100°C is not affected by lowering the sintering temperature. The figure of merit is ZT = 0.12 at 700°C for samples sintered at 1300°C; ZT = 0.08 and 0.03 were obtained for multilayer laminates sintered at 1050°C and 1000°C, respectively. A transversal multilayer thermoelectric generator (TMLTEG) was built by stacking layers of substituted CaMnO3 green tapes, and printing AgPd conductor stripes onto the thermoelectric layers at an angle of 30° relative to the direction of the heat flow. The multilayer stack was co-fired at 1000°C. The TMLTEG has a power output of 2.5 mW at ∆T= 200 K in the temperature interval of 25°C to 300°C. A meander-like generator with larger power output comprising six TMTEGs is also presented. This article is protected by copyright. All rights reserved.