Evaluation of fatigue properties for aged 9Cr-1Mo steel
2010
Low cycle fatigue tests of 9Cr-1Mo steel aged at 600°C for 5000 h and 10000 h were conducted at RT-600°C. Fatigue life was not decreased with aging. Cyclic softening was seen with cycles in both unaged and aged specimens. Aging decreased the amount of softening at RT and 400°C but increased it at 600°C. The precipitate species were not changed with aging upto 5000 h but Laves phase was precipitated after 10000 h aging. Fatigue life of 9Cr-1Mo steel aged to 10000 h is dependent on dislocation slip behavior rather than the amount and coarsening of precipitate.