Annealing effect of domain patterns of thel nearly non-magnetostrictive amorphous alloy Co58Ni10Fe5Si11B16
1982
The influence of different annealing conditions on the domain patterns of the nearly non-magneto-strictive amorphous alloy Co58Ni10Fe5Si11B16, is investigated by means of the longitudinal magneto optical Kerr effect. In the as-quenched and in the stress relieved ribbon the domain patterns are composed of wide domains. A conventional annealing treatment at low temperature (Ta < T) gives rise to the appearance of patches of narrow laminae, whereas an annealing treatment in a magnetic field perpendicular to the plane of the ribbon results in extended fingerprint-like domain patterns. From the field dependence of the domain width an induced magnetic anisotropy energy of K1 = 0.42 × 102 J/m3 is derived, a specific Bloch wall energy of γB = 3 × 10−5 J/m2 (0.03 erg/cm2), and a domain wall width of δB = 0.6 μm.
Der Einflus verschiedener Anlasbehandlungen auf die Domanenstruktur nahezu magnetostriktionsfreier amorpher Legierungen Co58Ni10Fe5Si11B16 wird mit Hilfe des longitudinalen magneto-optischen Kerreffektes untersucht. In der abgeschreckten und spannungsfrei gegluhten Probe besteht die Domanenstruktur aus ausgedehnten Domanen. Eine konventionelle Anlasbehandlung bei niedrigen Temperaturen (Ta < Tc) erzeugt Bereiche mit feinen Streifendomanen wahrend eine Anlasbehandlung in einem Magnetfeld senkrecht zur Bandebene ausgedehnte, fingerabdruckahnliche Domanenstrukturen hervorbringt. Aus der Peldabhangigkeit der Domanenweite wird eine induzierte Anisotropieenergie von K 1 = 0,42 × 102 J/m3, eine spezifische Wandenergie von γB = 3 × 10−5 J/m2 (0,03 erg/cm2) und eine Wanddicke von δB = 0,6 μm bestimmt.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
9
References
4
Citations
NaN
KQI