Low temperature rf sputtering deposition of (Ba, Sr) TiO3 thin film with crystallization enhancement by rf power supplied to the substrate

The (Ba, Sr) TiO3 thin film deposited by radio frequency (rf) sputtering requires a high deposition temperature near 500°C to realize a high relative dielectric constant over of 300. For example, the film deposited at 330°C contains an amorphous phase and shows a low relative dielectric constant of less than 100. We found that rf power supplied not only to the (Ba, Sr) TiO3 sputtering target, but also to the substrate during the initial step of film deposition, enhanced the crystallization of the (Ba, Sr) TiO3 film drastically and realized a high dielectric constant of the film even at low deposition temperatures near 300°C. The 50‐nm-thick film with only a 10nm initial layer deposited with the substrate rf biasing is crystallized completely and shows a high relative dielectric constant of 380 at the deposition temperature of 330°C. The (Ba, Sr) TiO3 film deposited at higher temperatures (upwards of 400°C) shows ⟨110⟩ preferred orientation, while the film deposited at 330°C with the 10nm initial layer sho...