Increase in the Magnetic Ordering Temperature (Tc) as a Function of the Applied Pressure for A2Mn[Mn(CN)6] (A = K, Rb, Cs) Prussian Blue Analogues
2017
Magnetization measurements under pressure reveal that the external hydrostatic pressure significantly increases in the ferrimagnetic transition temperature, Tc, for A2Mn[Mn(CN)6] (A = K, Rb, Cs). In the case of monoclinic A = K and Rb, dTc/dp values are 21.2 and 14.6 K GPa–1, respectively, and Tc increases by 53 and 39%, respectively, from ambient pressure to 1.0 GPa. The cubic A = Cs compound also shows a monotonous increase with an initial rate of 4.22 K GPa–1 and about 11.4 K GPa–1 above 0.6 GPa, and an overall Tc increase by 26% at 1.0 GPa. The increase in Tc is attributed to deformation of the structure such that the MnII—N≡C angle decreases with increasing pressure. The smaller the alkali cation, the greater the decrease in the MnII—N≡C angle induced by pressure and the larger the increase of dTc/dp. This is in accordance with the ambient-pressure structures for A2Mn[Mn(CN)6] (A = K, Rb, Cs), which have decreasing MnII—N≡C angles that correlate to the observed increasing Tcs as K > Rb > Cs. The larg...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
26
References
11
Citations
NaN
KQI