Phase Transformation and Superstructure Formation in (Ti0.5, Mg0.5)N Thin Films through High-Temperature Annealing

(Ti0.5, Mg0.5)N thin films were synthesized by reactive dc magnetron sputtering from elemental targets onto c-cut sapphire substrates. Characterization by θ–2θ X-ray diffraction and pole figure measurements shows a rock-salt cubic structure with (111)-oriented growth and a twin-domain structure. The films exhibit an electrical resistivity of 150 mΩ·cm, as measured by four-point-probe, and a Seebeck coefficient of −25 µV/K. It is shown that high temperature (~800 °C) annealing in a nitrogen atmosphere leads to the formation of a cubic LiTiO2-type superstructure as seen by high-resolution scanning transmission electron microscopy. The corresponding phase formation is possibly influenced by oxygen contamination present in the as-deposited films resulting in a cubic superstructure. Density functional theory calculations utilizing the generalized gradient approximation (GGA) functionals show that the LiTiO2-type TiMgN2 structure has a 0.07 eV direct bandgap.