Silica- and Alkoxysilane-Coated Ultrasmall Superparamagnetic Iron Oxide Particles: A Promising Tool To Label Cells for Magnetic Resonance Imaging

In this study silica- and alkoxysilane-coated ultrasmall superparamagnetic iron oxide (USPIO) particles were synthesized, and their ability to label immortalized progenitor cells for magnetic resonance imaging (MRI) was compared. USPIO particles were synthesized by coprecipitation of ferric and ferrous salts. Subsequently, the particles were coated with silica, (3-aminopropyl)trimethoxysilane (APTMS), and [N-(2-aminoethyl)-3-aminopropyl]trimethoxysilane (AEAPTMS). The size of the USPIO particles was about 10 nm without a significant increase in diameter after coating. The highest T2 relaxivity was achieved for silica-coated USPIO particles, 339.80 ± 0.22 s-1 mM-1, as compared with APTMS- and AEAPTMS-coated ones, reaching 134.40 ± 0.01 and 84.79 ± 0.02 s-1 mM-1, respectively. No toxic effects on the cells could be detected by trypan blue, TUNEL, and MTS assays. Uptake of USPIO particles was evaluated by Prussian blue staining, transmission electron microscopy, T2-MR relaxometry, and mass spectrometry. It w...