Structure and properties of α-NaFeO2-type ternary sodium iridates

Abstract The synthesis, structure, and elementary magnetic and electronic properties are reported for layered compounds of the type Na 3− x M Ir 2 O 6 and Na 3− x M 2 IrO 6 , where M is a transition metal from the 3 d series ( M =Zn, Cu, Ni, Co, Fe and Mn). The rhombohedral structures, in space group R −3 m , were determined by refinement of neutron and synchrotron powder diffraction data. No clear evidence for long range 2:1 or 1:2 honeycomb-like M /Ir ordering was found in the neutron powder diffraction patterns except in the case of M =Zn, and thus in general the compounds are best designated as sodium deficient α-NaFeO 2 -type phases with formulas Na 1− x M 1/3 Ir 2/3 O 2 or Na 1− x M 2/3 Ir 1/3 O 2 . Synchrotron powder diffraction patterns indicate that several of the compounds likely have honeycomb in-plane metal–iridium ordering with disordered stacking of the layers. All the compounds are sodium deficient under our synthetic conditions and are black and insulating. Weiss constants derived from magnetic susceptibility measurements indicate that Na 0.62 Mn 0.61 Ir 0.39 O 2 , Na 0.80 Fe 2/3 Ir 1/3 O 2 , Na 0.92 Ni 1/3 Ir 2/3 O 2 , Na 0.86 Cu 1/3 Ir 2/3 O 2 , and Na 0.89 Zn 1/3 Ir 2/3 O 2 display dominant antiferromagnetic interactions. For Na 0.90 Co 1/3 Ir 2/3 O 2 the dominant magnetic interactions at low temperature are ferromagnetic while at high temperatures they are antiferromagnetic; there is also a change in the effective moment. Low temperature specific heat measurements (to 2 K) on Na 0.92 Ni 1/3 Ir 2/3 O 2 indicate the presence of a broad magnetic ordering transition. X-ray absorption spectroscopy shows that iridium is at or close to the 4+ oxidation state in all compounds. 23 Na nuclear magnetic resonance measurements comparing Na 2 IrO 3 to Na 0.92 Ni 1/3 Ir 2/3 O 2 and Na 0.89 Zn 1/3 Ir 2/3 O 2 provide strong indications that the electron spins are short-range ordered in the latter two materials. Na 0.62 Mn 0.61 Ir 0.39 O 2 , Na 0.80 Fe 2/3 Ir 1/3 O 2 , Na 0.90 Co 1/3 Ir 2/3 O 2 , Na 0.92 Ni 1/3 Ir 2/3 O 2 , Na 0.86 Cu 1/3 Ir 2/3 O 2 and Na 0.89 Zn 1/3 Ir 2/3 O 2 are spin glasses. (CSD-numbers: Na 0.62 Mn 0.61 Ir 0.39 O 2 : 426657, Na 0.80 Fe 2/3 Ir 1/3 O 2 : 426659, Na 0.90 Co 1/3 Ir 2/3 O 2 : 426658, Na 0.92 Ni 1/3 Ir 2/3 O 2 : 426656, Na 0.86 Cu 1/3 Ir 2/3 O 2 : 426655, and Na 2.8 ZnIr 2 O 6 : 426660.)