Origin of anomalously high exchange field in antiferromagnetically coupled magnetic structures: Spin reorientation versus interface anisotropy

Magnetization reorientation from in-plane to perpendicular direction, observed in Co thin film coupled antiferromagnetically to high perpendicular magnetic anisotropy (Co/Pd) multilayers, is studied systematically for Co thickness ranging from 0 to 2.4 nm. The sample with 0.75 nm thick Co showed an exchange coupling field (Hex) exceeding 15 kOe at room temperature and 17.2 kOe at 5 K. With an increase of Co thickness, Hex decreased as expected and beyond certain thickness, magnetization reorientation was not observed. Indeed, three regions were observed in the thickness dependence of magnetization of the thin layer; one in which the thin layer (in the thickness range up to 0.8 nm) had a perpendicular magnetic anisotropy due to interface effects and antiferromagnetic coupling, another in which the thin layer (0.9–1.2 nm) magnetization had no interface or crystallographic anisotropy but was reoriented in the perpendicular direction due to antiferromagnetic coupling, and the third (above 1.2 nm) in which the...