An iron phosphate composition for vitrifying a high sulfate (~17 wt%) and high alkali (~80 wt%) Hanford low activity waste (LAW), known as AZ-102 LAW, has been developed for processing in a Joule Heated Melter (JHM) or a Cold Crucible Induction Melter (CCIM). This composition produced a glass waste form, designated as MS26AZ102F-2, with a waste loading of 26 wt% of the AZ-102 which corresponded to a total alkali and sulfate (represented as SO3) content of 21 and 4.4 wt%, respectively. A slurry (7M Na + ) of MS26AZ102F-2 simulant was melted continuously at temperatures between 1030 and 1090°C for 10 days in a small JHM at PNNL and for 70 hours in a CCIM at INL. The as-cast glasses produced in both melters and in trial laboratory experiments along with their canister centerline cooled (CCC) counterparts met the requirements for the Product Consistency Test (PCT) and the Vapor Hydration Test (VHT) responses in the Hanford Tank Waste Treatment and Immobilization Plant (WTP) Contract. These glass waste forms retained up to 77 % of the SO3 (3.3 wt%), 100% of the Cesium, and 33 to 44% of the rhenium (used as a surrogate for Tc) all of which either exceeded or were comparable to the retention limit for these species in borosilicate glass nuclear waste form. Analyses of commercial K-3 refractory lining and the Inconel 693 metal electrodes used in JHM indicated only minimum corrosion of these components by the iron phosphate glass. This is the first time that an iron phosphate composition was melted continuously in a slurry fed JHM and in the US, thereby, demonstrating that iron phosphate glasses can be used as alternative hosts for vitrifying nuclear waste.
In this paper, we demonstrate a fiber pigtailed thin wall capillary coupler for excitation of Whispering Gallery Modes (WGMs) of microsphere resonators. The coupler is made by fusion-splicing an optical fiber with a capillary tube and consequently etching the capillary wall to a thickness of a few microns. Light is coupled through the peripheral contact between inserted microsphere and the etched capillary wall. The coupling efficiency as a function of the wall thickness was studied experimentally. WGM resonance with a Q-factor of 1.14 × 10(4) was observed using a borosilicate glass microsphere with a diameter of 71 μm. The coupler operates in the reflection mode and provides a robust mechanical support to the microsphere resonator. It is expected that the new coupler may find broad applications in sensors, optical filters and lasers.
A high priority has been given to investigating the vitrification of three specific nuclear wastes in iron phosphate glasses (IPG). These wastes, which were recommended by the Tank Focus Area (TFA) group of Hanford, are poorly suited for vitrification in the currently DOE-approved borosilicate (BS) glasses. They include (1) a sodium bearing waste (SBW) at INEEL, (2) a high chrome waste (HCW) at Hanford, and (3) a high sodium/sulfate waste (HSSW), also known as low activity waste (LAW) at Hanford. A simulated composition for each waste, which was simplified by neglecting components present in quantities < 0.4 wt%, was used in the present investigation.
A porous-wall hollow glass microsphere (PW-HGM) was investigated as an optical resonator for chemical vapor sensing. A single mode optical fiber taper was used to interrogate the microresonator. Adsorption of chemical molecules into the nanosized pores induced a refractive index change of the thin wall and thus a shift in its resonance spectrum. The PW-HGM resonator had shown higher vapor detection sensitivity in comparison with a solid microsphere under similar test conditions.