Interaction mechanisms between polycarboxylate superplasticizers and cement, and the influence of functional groups on superplasticizer performance: a review
6
Citation
38
Reference
10
Related Paper
Citation Trend
Keywords:
Superplasticizer
Cementitious
By using XRD、SEM and other experimental methods, some details of polycarboxylate superplasticizer on the hydration products and performance of phosphogypsum-based cement(PBC) can be obtained. It can be found that the polycarboxylate superplasticizer makes the structure of the cement stone more compact, and significantly increases the strength of the cement. Besides, it can also improve the anti-carbonation and degradation properties of that cement.
Phosphogypsum
Superplasticizer
Degradation
Cite
Citations (8)
The incompatibility between the superplasticizer (SP) and cement can cause problems with the cementitious materials' fresh and hardened qualities, such as unstable workability, uncontrollable setting times, excessive air entrainment, and so on. In this paper, five various types of SPs were prepared. Their interaction with pure tricalcium aluminate (C3A) and its hydration products were investigated and their effect on the generation of Ettringite (AFt) and single-sulfur calcium sulphoaluminate hydrate (AFm) in paste and their compatibility with cement were also studied. The results demonstrate that after 15 min of cement hydration, the AFt and AFm content of mixture with polycarboxylate SP and sulfonated acetone-formaldehyde superplasticizer (PCA-SAF) is 124.6% and 24.8% higher than that of SAF, respectively, which decreases the consumption of SPs molecules and improves the compatibility of SAF with cement. Compared with polynaphthalene sulfonate superplasticizer (PNS), PCA-PNS dramatically enhanced the SP's compatibility with cement. Accelerating the production of AFt and AFm during the early stages of cement hydration may be one method to increase SP–cement compatibility.
Superplasticizer
Ettringite
Cementitious
Aluminate
Portlandite
Cite
Citations (2)
Because of less thorough study on the properties of cement pastes with superplasticizers and latex mixed together,the influence of different mixing procedures of superplasticizers and latex on the ζ potential of cement pastes(fresh) were analyzed using the ZetaProbe instrument.The experimental results show that with adding different use level(by mass) of polycarboxylic superplasticizer(PC),the cement pastes with both PC and latex added have negative or positive ζ potential.However,the ζ potential of cement pastes with both naphthalene formaldehyde condensate superplasticizer(NF) and latex added is lower than that of cement pastes with NF added but higher than that of cement pastes with latex added.Adding NF into cement pastes with latex added,the absolute value of equilibrium ζ potential of the cement pastes is lower than that of cement pastes with NF added,cement pastes with latex added and cement pastes with both NF and latex added.Adding PC into cement pastes with latex added,the ζ potential of the cement pastes can even reach the equilibrium ζ potential of cement paste with latex added.When latex is added in,the ζ potential of cement paste with 1.0% PC added doesn't change,but the ζ potential of cement paste with 0.1% PC added decreases greatly to a certain value.The ζ potential of cement paste with NF added increases from-10 mV to-6 mV when latex is added in,and then increases slowly with the increase of use level of latex.By adding superplasticizer(NF or PC) and latex into cement pastes simultaneously or adding latex into cement pastes with superplasticizer(NF or PC) added,the adsorbed proportion of polymer particles on cement grains can be decreased.
Superplasticizer
Zeta potential
Cite
Citations (2)
The article presents the results of researching efficiency of different modes of superplasticizer introduction in solution mixture with different consistency - from hard to plastic. The following methods of superplasticizer introduction into cement were researched: co-grinding of superplasticizer with cement, mixing cement with superplasticizer in dry state, introduction of superplasticizer into cement with mixing water, evaluation of water reduction effect of an additive depending on the methods of its introduction into cement and the time of determining its consistency. It is established that the most efficient method of superplasticizer introduction into plastic mixture is its co-grinding with cement.
Superplasticizer
Cite
Citations (0)
Superplasticizer
Cementitious
Water reducer
Shrinkage
Cite
Citations (9)
Abstract The article presents a comparative analysis on the hydration of cement paste without superplasticizer and water/cement ratio of 0.35 and a cement paste with the same water/cement ratio but has in its composition 2% superplasticizer additive Glenium Sky 526. For characterizing the hydration process of cement paste, both mixtures were subjected to X-ray diffraction and thermogravimetry analysis, at 3, 7, and 28 days passed since the initiation of hydration process.
Superplasticizer
Thermogravimetry
Water–cement ratio
Cite
Citations (3)
Silica fume
Superplasticizer
Cementitious
Plasticizer
Cite
Citations (1)
Superplasticizer
Cementitious
Cite
Citations (446)
In order to settle the technical and economical problem that Polycarboxylate Based Superplasticiaer(PC) is used in the concrete construction.The concrete of C10-C60 was prepared with four different cementitious material systems and seven different composition of cementitious material.And then under the circumstances of the same cementitious material system,the authors choose three different plasticizers(PC,lignosulphate based plasticizer(LS) and naphthalene sulphate based superplasticizer(NSF)) for mixing concrete of the same compressive strength and compared their technicality and cost of the raw materials.The results indicate that good performance can be obtained with the use of PC and ideal economy efficiency exists in high strength concrete added with PC.
Superplasticizer
Cementitious
Plasticizer
Cite
Citations (0)