Effect of Structure and Texture on Failure of Pipe Steel Sheets produced by TMCP

The method of orientation microscopy (EBSD) is used to study the structure and texture of low-carbon, low-alloy pipe steel sheets processed by controlled thermomechanical processing (TMCP). The temperatures of isothermal hot rolling varied. Samples cut from sheets showed a different fracture tendency during mechanical testing. The formation of cleavages (secondary cracks) during failure of steel is related to the presence of ferrite grains with orientation {001} extended in the hot rolling direction. The formation of grains is a consequence of the isothermal hot rolling below the temperature A