Improvement of GaN epilayer by gradient layer method with molecular-beam epitaxy

Abstract We demonstrated a molecular beam epitaxy method to resolve the dilemma between structural and morphological quality in growth of the GaN epilayer. A gradient buffer layer was grown in such a way that the N/Ga ratio was gradually changed from nitrogen-rich to gallium-rich. The GaN epitaxial layer was then grown on the gradient buffer layer. In the X-ray diffraction analysis of GaN(002) rocking curves, we found that the full width at half-maximum was improved from 531.69″ to 59.43″ for the sample with a gradient buffer layer as compared to a purely gallium-rich grown sample. Atomic force microscopy analysis showed that the root-mean-square roughness of the surface was improved from 18.28 nm to 1.62 nm over an area of 5 × 5 μm 2 with respect to a purely nitrogen-rich grown sample. Raman scattering showed the presence of a slightly tilted plane in the gradient layer. Furthermore we showed that the gradient layer can also slash the strain force caused by either Ga-rich GaN epitaxial layer or AlN buffer layer.