MgxZn1-xO/Ag/MgxZn1-xO Multilayers As High-Performance Transparent Conductive Electrodes.
2016
We report on the optical and electrical properties of MgxZn1–xO/Ag/MgxZn1–xO transparent conductive electrodes. The transmittance and sheet resistance of MgxZn1–xO/Ag/MgxZn1–xO multilayers deposited at room temperature were strongly dependent on the thickness and surface morphology of Ag layer. The optical absorption edge of MgxZn1–xO/Ag/MgxZn1–xO showed a blue shift with increasing Mg composition due to the increased band gap of MgxZn1–xO. The Haack figure of merit value of Mg0.28Zn0.72O/Ag/Mg0.28Zn0.72O with a 14 nm-thick Ag layer, which has a sheet resistance of 6.36 Ω/sq and an average transmittance of 89.2% at wavelengths in the range from 350 to 780 nm, was 69% higher than that of a ZnO/Ag/ZnO multilayer electrode. These results indicate that MgxZn1–xO/Ag/MgxZn1–xO multilayers, which also show low surface roughness, can be used as highly conductive transparent electrodes in various optoelectronic devices operating over a wide wavelength region.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
31
References
29
Citations
NaN
KQI