Influence of solid loading on densification behavior, micromorphology and dielectric properties of Ba0.67Sr0.33TiO3 ceramics fabricated by a novel DCC-HVCI method

Abstract Ba0.67Sr0.33TiO3 (BST) ceramics with highly improved dielectric performance were fabricated by a novel direct coagulation casting via high valence counter ions (DCC-HVCI) method. The influence of solid loading on densification behavior, micromorphology, and dielectric performance of the samples was investigated. With the increase of solid loading from 40 to 50 vol%, the maximum densification rate of BST ceramics increased from 0.090 to 0.122 s−1, and the densification temperature decreased from 1424 to 1343 °C, which indicated that high solid loading could promote the densification behavior of samples during sintering. BST ceramics fabricated by the DCC-HVCI method showed uniform grain size and microstructure, which was beneficial for the dielectric properties of BST ceramics. Samples obtained from 45 vol% suspensions possessed the lowest dielectric permittivity (er ≈ 2801), and the dielectric loss (tanδ≈0.0262) was about 1/10 of that of dry-pressed samples (tanδ≈0.301), which could be attributed to the composition homogenization.