Effects of aging temperature on G-phase precipitation and ferrite-phase decomposition in duplex stainless steel

G-phase precipitation and ferrite-phase decomposition in a cast duplex stainless steel (DSS) aged at 623–723 K for up to 8000 h were investigated using atom probe tomography (APT). Large sample volume was observed in every APT experiment, which yielded significantly statistical results. The number density of G-phase precipitates tended to be high and their sizes were small at lower aging temperatures. G-phase precipitates grew during prolonged isothermal aging. The concentrations of nickel, silicon, manganese and molybdenum in G-phase precipitates tended to increase as the precipitates grew. Heterogeneous distributions of alloying elements within G-phase precipitates were observed. An interesting positional relationship of G-phase precipitates with dislocations was revealed. Regarding the ferrite-phase decomposition, local chromium concentrations in the ferrite phase varied fast at higher aging temperatures. Good correlation between the variation of local chromium concentrations and aging conditions was r...