Microstructure and mechanical behavior of low-melting point Bi-Sn-In solder joints

Ternary Bi-31.5Sn-25.0In solder has been proposed and studied for application in temperature-sensitive electronic components. In a Bi-31.5Sn- 25.0In solder joint, In was detected in an intermetallic compound (IMC) layer formed at the solder/Cu substrate interface with a thickness of 4.8 μm. The microstructure of the bulk solder consisted of Sn-rich phases distributed in Bi-rich phases with dispersion of In in both phases. Meanwhile, the nanomechanical properties of the Bi-31.5Sn-25.0In solder showed great strain rate sensitivity. To be specific, hardness increased from 9.91 MPa to 56.84 MPa as the strain rate increased in the range of (0.0005-0.125) s−1. The strain-rate sensitivity exponent (m) was found to be 0.28, indicating that the excellent ductility was shown for the solder tested under the present conditions. Open image in new window