CORROSION AT THE HEAD-TRUNNION TAPER INTERFACE IN LARGE DIAMETER HEAD METAL-ON-METAL TOTAL HIP ARTHROPLASTY: A COMPARISON OF FIVE MANUFACTURERS

Corrosion at the taper interface between the femoral head and the femoral stem is well described in metal-on-polyethylene (MoP) hips but previously was undetermined in large diameter head metal-on-metal (LHMoM) hips. The high failure rate of the articulating surface replacement (ASR) XL hip system has been partly attributed to susceptibility to corrosive damage at the taper interface. It was not known if other hip manufacturers are liable to taper corrosion. Therefore the aim of this study was to quantify the prevalence and severity of taper corrosion in LHMoM hips and compare corrosion across five different current generation manufacturers.Taper corrosion was analysed in a consecutive series of the five most common hip types at our retrieval centre: ASR XL, DePuy (n=49); Birmingham hip resurfacing, Smith & Nephew (n=33), Durom, Zimmer (n=31), M2a Magnum, Biomet (n=14) and Cormet, Stryker (n=10). A four-scale peer-reviewed qualitative corrosion scoring system was used to quantify corrosion (none, mild, mo...