Dislocation loops in AlZn and AlZnMg alloys

The existence and nature of dislocation loops (DL) and the heterogeneous nucleation of precipitates at them are studied in three Al-(3.0, 12 and 15 at%) Zn as well as in two AlZn(2x)-Mg(x) alloys (x = 1.0 and 1.5at%) using TEM. The most important results are: (i) Not only in the AlZn, but also in the AlZnMg alloys DL are observed, although in the latter, according to the literature their formation is not expected, (ii) The heterogeneous nucleation of precipitates is proceeding in quite a different manner in both alloy systems. The reasons supposed are discussed. In drei AlZn-(xzn = 3,0; 12 und 15 At%) als auch in zwei AlZn(2x)-Mg(z)-Legierungen (x = 1,0 und 1,5 At%) werden mittels TEM die Existenz und die Natur von Versetzungsschleifen (DL) und die heterogene Keimung von Ausscheidungen an ihnen untersucht. Die wichtigsten Ergeb-nisse sind: (i) Nicht nur in den AlZn-, sondern auch in den AlZnMg-Legierungen werden DL beobachtet, obwohl in den zuletzt genannten Legierungen ihr Auftreten nach Literaturmeinung nicht zu erwarten ist. (ii) Die heterogene Keimung von Ausscheidungen an den DL verlauft in den AlZn-Legierungen ganz anders als in denen mit Magnesiumzugaben. Die vermuteten Grunde werden diskutiert.