Microstructure of aluminized stainless steel 310 after annealing

Abstract The aluminized coating on type 310 stainless steel prepared by high-activity Al pack cementation method has been annealed at 900 °C for 12 h to transform the brittle δ-Fe 2 Al 5 phase into the more ductile β-FeAl phase. The microstructure is studied in detail with transmission electron microscopy. The thick outer layer has β-(Fe, Ni)Al as matrix with cube-like Cr 2 Al precipitates. The interfacial layer has a thin layer of metastable FCC phase (layer I) and then mixed β-(Fe, Ni)Al grains and α-(Fe, Cr) grains (layers II and III). The Cr 2 Al precipitates are present in the β-(Fe, Ni)Al grains in layer II but not in those in layer III, while β-FeAl precipitates are present in the α-(Fe, Cr) grains in both layers. The orientation relationships between various phases, the formation of the layers, and the precipitation of Cr 2 Al in β-(Fe, Ni)Al are discussed.