Novel SnSb2S4 Thin Films Obtained by Chemical Bath Deposition using Tartaric Acid as Complexing Agent for Their Application as Absorber in Solar Cells
2019
Ternary Sn-Sb-S thin films with remarkable optical, electrical and structural properties were developed by chemical bath deposition. Tin and antimony chlorides and thioacetamide were used as tin, antimony, and sulfur ion sources, respectively, while tartaric acid was used as a complexing agent. XRD analysis of as-deposited films showed a combination of binary phases of SnS, Sn2S3, and Sb2S3, while after thermal treatment in nitrogen at 400 °C, the films became crystalline showing well-defined reflections of the ternary SnSb2S4. The heating also influenced the morphology, compactness, and thickness of the films. On the other hand, all the films showed an absorption coefficient higher than 104 cm-1, while the optical band gap of the as-deposited film decreased from 1.49 to 1.37 eV after heating at 400 °C. In addition, the photoconductivity of the films prior to heating was of 10-9 Ω-1 cm-1, while after that at 400 °C was of 10-7 Ω-1 cm-1. The evaluation of the ternary film in solar cells gave an open-circuit voltage Voc of 448 mV and short-circuit current density of Jsc of 2.4 mA/cm2.
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
18
References
3
Citations
NaN
KQI