Conformation and electrical conductivity of poly(γ‐methyl‐L(LD)‐glutamates) reticulate‐doped with 1,3‐dimethylimidazolium‐7,7,8,8‐tetracyano‐p‐quinodimethane complex salt

Polymeric composites were prepared by reticulate doping of poly(γ-methyl-L-glutamate) (PMLGA) and poly(γ-methyl-LD-glutamate) (PMLDGA, 1 : 1) having different conformation forms with 1,3-dimethylimidazolium-TCNQ complex salt. The heat induced α-helix to coil transition in PMLGA and α-helix to β-form and coil transition in PMLDGA were carried out in chlorobenzene and o-dichlorobenzene at temperatures between 70 and 150°C. The conductivity of polyglutamate composites thermally treated and prepared at 70°C is higher by approximately two orders of magnitude than that of thermally not treated films cast at ambient temperature. The conductivity of the most conductive reticulate-doped PMLGA film is higher by more than four orders of magnitude than that of the 1,3-dimethylimidazolium-TCNQ complex salt in pressed pellets. Poly(γ-methyl-L-glutamat) (PMLGA) und Poly(γ-methyl-LD-glutamat) (PMLDGA, 1:1) mit unterschiedlicher Konformation wurden mit einem 1,3-Dimethylimidazolium-TCNQ-Komplexsalz dotiert. Der warmeinduzierte Konformationsubergang von der α-Helix zur Spiralform (PMLGA) bzw. zur β- und Spiralform (PMLDGA) wurde in Chlorbenzol und o-Dichlorbenzol bei Temperaturen zwischen 70 und 150°C durchgefuhrt. Die Leitfahigkeit der bei 70°C hergestellten und warmebehandelten Polyglutamat-Composite ist um etwa zwei Zehnerpotenzen besser als die der bei Raumtemperatur gegossenen, thermisch nicht behandelten Filme. Die Leitfahigkeit des leitfahigsten dotierten PMLGA-Films ist um mehr als vier Zehnerpotenzen groser als die des zu Tabletten gepresten 1,3-Dimethylimidazolium-TCNQ-Komplexsalzes.