Mössbauer investigation of the influence of Al(III) ions on the properties of mixed Fe(III)–Al(III) hydroxides and oxides

Phase composition and components of mixed Fe(III)–Al(III) hydroxides and oxides obtained by ageing the hydroxides are examined mainly by Mossbauer spectroscopy over a wide range of the Al/Fe atomic ratio. The α-(Fe1–cAlc)2O3 type oxide and the orthorhombic Al2O3, boehmite, are identified in the system studied. An analysis of Heff as a function of c indicates that the maximum value of c ranges from 0.31 to 0.33 regardless of the mixed oxide preparation method. An analysis of the recoil-free fraction f′(T) and a subsequent calculation of the force constants of the iron–oxygen bonds show that an increase in “c” leads to their weakening. Hauptsachlich mittels Mosbauerspektroskopie werden uber einen grosen Bereich des Al/Fe-Atomverhaltnisses Phasenzusammensetzung und Komponenten der Fe(III)–Al(III)-Mischhydroxide und der durch Alterung der Hydroxide erhaltenen Oxide untersucht. Im untersuchten System werden das α-(Fe1–cAl)2O3-Oxid und das rhombische Al2O3-Boehmit identifiziert. Eine Analyse von Heff als Funktion von c zeigt, das der Maximalwert von c von 0,31 bis 0,33 reicht, unabhangig von der Praparationsmethode der Mischoxide. Eine Analyse des ruckstosfreien Anteils f′(T) und eine folgende Berechnung der Kraftkonstanten der Eisen–Sauerstoff-Bindungen zeigen, das ein Anwachsen von c zu ihrer Erweichung fuhrt.