Differential Thermal Analysis of Hg(1-x)Mn(x)Te Alloys in the X=0 to 0.3 Range

Understanding the experimental conditions necessary for the development of radial and axial compositional homogeneity in directionally solidified Hg(0.89)Mn(0.11)Te(MMT) crystals has been difficult due to the lack of segregation coefficient data on the Hg(1-x)Mn(x)Te alloy system in the X = 0 to 0.3 composition range. Determining segregation coefficient data from the available Hg(1-x)Mn(x)Te alloy phase equilibria data is not practical due to discrepancies in the shape of the reported solidus and liquidus curves in the X = 0 to 0.3 range. To resolve these discrepancies and to obtain segregation coefficient data which can be used to understand homogeneity in directionally solidified MMT crystals, the solidus and liquidus temperatures of seven Hg(1-x)Mn(x)Te alloys in the X = 0 to 0.3 range were determined using differential thermal analysis (DTA). The Hg(1-x)Mn(x)Te phase diagram constructed for the X = 0 to 0.3 range of this alloy system from the DTA measurements clarifies the shape of the solidus and liquidus curves in this range. The segregation coefficient for the Hg(1-x)Mn(x)Te system was found to vary from 5 to 4.4 as the solidus composition increased from 0-30 atomic percent MnTe. This information will be useful in the analysis of axial and radial homogeneity of directionally solidified MMT crystals.