Secondary corrosion protection of FeCr(Al) model alloys at 600 °C – The influence of Cr and Al after breakaway corrosion

Abstract The influence of Cr and Al content on the oxidation behaviour of FeCr(Al) model alloys after breakaway oxidation at 600 °C and the underlying mechanisms were investigated in detail with thermogravimetrical analysis (TGA), thermodynamic calculations and advanced electron microscopy. The results showed that a Cr-content of ≥18 wt% drastically reduced the growth rate of the Fe-rich oxide scale, formed after breakaway oxidation, for FeCrAl alloys but not for FeCr alloys. This was attributed to the ability of the Fe(18-25)CrAl alloys to prevent internal oxidation, which enables the formation of a healing layer.