STRATURI NANOSTRUCTURATE DE ZnO DOPATE CU Al PENTRU FOTOELECTROZI ÎN STRUCTURILE HIBRIDE PE BAZA FTALOCIANINEI DE CUPRU

In articol este prezentat un studiu al structurii si proprietăţilor optice ale straturilor subţiri de ZnO dopate cu Al atât netratate termic, cât si tratate termic in flux de hidrogen la 445 o C, precum si proprietăţile electrice ale structurilor pe baza acestora. Structura acestor straturi a fost făcută utilizând difracţia de radiaţii X, iar proprietăţilor lor optice – prin spectroscopia UV-VIS. S-a constatat că straturile ZnO:Al au structură policristalină de tip wutzite; dimensiunea crista­litelor depinde de regimul tehnologic. Cu cresterea concentraţiei de Al dimensiunea acestora se micsorează, iar tratarea termică in hidrogen conduce la micsorarea valorii E g indiferent de regimul tehnologic de fabricare a straturilor subţiri. Au fost realizate structuri ZnO/CuPc si cercetate proprietăţile lor electrice utilizând caracteristicile curent-tensiune si capacitate-tensiune. Dependenţa capacităţii de tensiune justifică prezenţa regunii de sarcină spaţială. NANOSTRUCTURED ZnO THIN FILMS DOPED WITH Al FOR PHOTOELECTRODS IN THE HYBRID STRUCTURES BASED ON THE COPPER  PHTALOCYANINE In this paper, a study of the structure and optical properties of ZnO thin films doped with Al, both untreated and treated in hydrogen at 445oC, as electrical properties of structures based on them it is presents. Studies on the structure and optical properties were made using X-ray diffraction and UV-VIS spectroscopy. It was found that the ZnO: Al layers were polycrystalline and have a wurtzite structure, crystallite size depends on the technological regime, with increasing concentration of Al their size decreases and annealing in hydrogen leads to decrease in E g value indifferently of the manufacturing technology. ZnO/CuPc structures were fabricated. Their electrical properties using current-voltage and capacitance-voltage characteristics were investigated. The capacitance-voltage characteristics justify the presence of a space charge region.