Engineered defects for investigation of laser-induced damage of fused silica at 355 nm

Embedded gold and mechanical deformation in silica were used to investigate initiation of laser-induced damage at 3.55-nm (7.6 ns). The nanoparticle-covered surfaces were coated with between 0 and 500 nm of SiO{sub 2} by e-beam deposition. The threshold for observable damage and initiation site morphology for these ''engineered'' surfaces was determined. The gold nanoparticle coated surfaces with 500nm SiO{sub 2} coating exhibited pinpoint damage threshold of <0.7 J/cm{sup 2} determined by light scattering and Nomarski microscopy. The gold nanoparticle coated surfaces with the 100nm SiO{sub 2} coatings exhibited what nominally appeared to be film exfoliation damage threshold of 19 J/cm{sup 2} via light scattering and Nomarski microscopy. With atomic force microscopy pinholes could be detected at fluences greater than 7 J/cm{sup 2} and blisters at fluences greater than 3 J/cm{sup 2} on the 100 nm-coated surfaces. A series of mechanical indents and scratches were made in the fused silica substrates using a nano-indentor. Plastic deformation without cracking led to damage thresholds of -25 J/cm{sup 2}, whereas indents and scratches with cracking led to damage thresholds of only {approx}5 J/cm{sup 2}. Particularly illuminating was the deterministic damage of scratches at the deepest end of the scratch, as if the scratch actedmore » as a waveguide.« less