Shape-controlled synthesis of hydroxyapatite from α-tricalcium bis(orthophosphate) in organic-aqueous binary systems
2002
Hydrolyses of α-tricalcium bis(orthophosphate) Ca3(PO4)2 (α-TCP) were carried out in a heterogeneous solvent system (hydrophobic organic solvent-water). The hydroxyapatites (HAp) formed were deficient in calcium (Ca/P = 1.56–1.61, a-axis = 0.9440 nm, c-axis = 0.6880 nm) and contained acid phosphate (and sometimes carbonate depending on the organic solvent used). The HAp was in the form of needles with a length (1–4 μm) that depended on the polarity of the hydrophobic organic solvent. The aspect ratio was highest in 1-octanol with a polarity of ET = 48.3. On the other hand, in a hydrophobic organic solvent system without OH groups such as n-octane (ET = 31.1), HAp formed fine particles that are similar to HAp prepared in a system without an organic solvent. Thus, hydrophobicity and OH groups of organic solvents affect the crystal growth of HAp.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
5
References
15
Citations
NaN
KQI