Comparison of Lini 0.5 Mn 1.5 O 4 and LiMn 2 O 4 for Lithium-Ion Battery
2013
The High Potential Material Lini0.5Mn1.5O4 was Synthesized via Solid-State Reaction.The Surface Morphology and Particle Size of the Sample were Observed by Scanning Electron Microscope(SEM).The Crystal Structure of the Sample was Collected and Analyzed through X-Ray Diffractometry(XRD).The Sample was Charaterized by Charge-Discharge Tests.Results Indicated that the Cycling Retention Rate was about 80%,after being Charge-Diacharged at a Rate of 0.1C in a Voltage of 3.45-4.77V for 10 Times.Compared with Limn2O4,LiNi0.5Mn1.5O4 has good cycle performance.Both of LiNi0.5Mn1.5O4 structure were space group of Fd3m.