Irradiation-induced precipitation in a SUS316 stainless steel using three-dimensional atom probe

Abstract Precipitation and segregation were investigated in a compositionally modified 316 austenitic stainless steel, neutron-irradiated at 862 K using a three-dimensional atom probe. In the solution-annealed specimen, Mo, Ti, Nb, C and P enrichment were observed in a silicide, with nominal composition Fe 3 Cr 2 Ni 2 Mo 2 Si 2 . In a Ti-rich carbide, nominaling Fe 5 Cr 8 Ni 10 Mo 2 Ti 11 Si 2 C 6 , enrichment of Mo, Si, O, and Nb was observed. Radiation-induced segregation (RIS) at the precipitate–matrix interface was also investigated at an atomic scale. RIS of Ni and P atoms, which are undersized in Fe, was also analyzed around the interface of the Ti-rich carbide and matrix. Results suggest that the carbide–matrix interface is a sink with an interstitial bias. In the cold-worked specimen, complex-precipitates consisting of silicide and carbide were formed.