Miscibility of polyarylate/phenoxy/poly(butyleneterephthalate) ternary blends

The phase and miscibility behavior of binary and ternary blends containing polyarylate (PAR), polyhydroxyether of bisphenol A1 (Phenoxy), and poly(butylene terephthalate) (PBT) were studied. The blends were prepared by solution-precipitation method and miscibility was examined by DSC and melt transparency. In binary blends, PAR/PBT and Phenoxy/PBT blends show miscibility, while PAR/Phenoxy appeared to be immiscible. However, the miscibility of incompatible PAR/Phenoxy blend was enhanced by addition of PBT. The addition of sufficient amount of PBT caused the ternary blend to have a single glass transition temperature. The shape of miscibility boundary of ternary blend was skewed to the apex of Phenoxy, which was attributed to the better miscibility of PAR/PBT than that of Phenoxy/PBT. Das Phasen- und Mischbarkeitsverhalten der binaren und ternaren Polymermischungen von Polyarylat (PAR), Phenoxid und Poly(butylenterephthalat) (PBT) wurde untersucht. Die Mischungen wurden durch Ausfallen aus gemeinsamen Losungen hergestellt, und die Mischbarkeit wurde durch DSC-Messungen und Transparenz der Schmelze beurteilt. Im Falle der binaren Blends zeigten PAR/PBT und Phenoxid/PBT Mischbarkeit, wahrend sich PAR/Phenoxid nicht mischen lies. Die Mischbarkeitstendenz der unmischbaren PAR/Phenoxid-Mischungen konnte jedoch durch Zugabe von PBT erhoht werden; eine ausreichende Menge PBT machte die ternaren Mischungen mischbar, so das diese eine einzige Tg in der DSC-Kurve zeigten. Im ternaren Phasendiagramm war das Maximum der Mischbarkeitsgrenze in Richtung auf die Phenoxidseite hin verschoben, was auf die bessere Mischbarkeit von PAR/PBT im Vergleich zu Phenoxid/PBT zuruckgefuhrt wird.