Characterization of microstructure of A508III/309L/308L weld and oxide films formed in deaerated high-temperature water

Abstract The microstructure of A508III/309L/308L weld clad and the properties of the oxide films formed in simulated pressurized water reactor primary water at 290 °C were characterized. The A508III heat-affected zone (HAZ) consisted primarily of a decarburization zone with ferrite near the fusion line and a following pearlite structure with fine grains. A high hardness region in the HAZ could be the result of C-enrichment. M 23 C 6 and M 7 C 3 precipitates were observed in element transition zone. 308L stainless steel (SS) containing ∼ 12% ferrites exhibited both ferritic-austenitic solidification mode (FA mode, δ→γ) and austenitic-ferritic solidification mode (AF mode, γ→δ), whereas 309L SS containing ∼ 9% ferrites exhibited only FA mode. The A508III surface oxide film was mainly Fe 3 O 4 in deaerated high-temperature water. The coarse grain zone covered with few oxide particles was different from other types of film on the other region of HAZ and the bulk zone. More pitting appears on 309L SS after immersion in deaerated high-temperature water due to the dissolution of inclusions. SS surface oxide films consisted primarily of spinels. The oxide film on SS was divided into two layers. Ni was concentrated mainly at the oxide/substrate interface. The oxide film formed on 309L was thicker than that on the 308L. The ferrite in the stainless steel could improve the oxidation resistance.