Inhibition of the detrimental double vortex-kink formation in thick YBa2Cu3O7 films with BaZrO3 nanorods

We investigated the temperature (T) variation of the normalized magnetization relaxation rate S and of the corresponding normalized vortex-creep activation energy U* = T/S for YBa2Cu3O7 films containing BaZrO3 nanorods, with the external magnetic field H oriented perpendicular to the film surface. It was found that by increasing the film thickness and using nanodot decorated substrates the high-T S(T) maximum appearing at low H is substituted by a minimum in S(T). As revealed by the analysis of the current density dependence of U*, this behaviour is due to the inhibition of vortex excitations involving double vortex-kinks and superkinks formation in the investigated thick films, owing to the large nanorod splay and pinning energy dispersion.