The modulation of oxygen vacancies by the combined current effect and temperature cycling in La0.7Sr0.3CoO3 film

Modulating the oxygen defect concentration has been accepted as an effective method to obtain high catalytic activity in perovskite cobaltites. However, controllably modifying the oxygen vacancy is still a challenge in this type of materials, which strongly obstructs their application. Here, we report a successful oxygen vacancies modulation in the La0.7Sr0.3CoO3 (LSCO) film by using combined current effect and temperature cycling. The temperature dependent transport properties of the LSCO/LAO film were investigated. The results revealed that the resistance of the film keeps increasing under the repeated measurements. It was found that the accumulation of the oxygen vacancy by current effect transforms the Co4+ ion into Co3+ ion, which results in the enhancement of the resistance and thus the transport switching behavior. Moreover, the resistance in the cooling process was found to be much higher than that in previous cooling and heating processes, which indicates that the oxygen escapes more quickly in t...