Surface Structure of Molecular Beam Epitaxy (211)B HgCdTe
2007
The as-grown molecular beam epitaxy (MBE) (211)B HgCdTe surface has variable surface topography, which is primarily dependent on substrate temperature and substrate/epilayer mismatch. Nano-ripple formation and cross-hatch patterning are the predominant structural features observed. Nano-ripples preferentially form parallel to the \( [\bar {1}11] \) and are from 0 A to 100 A in height with a wavelength between 0.1 μm and 0.8 μm. Cross-hatch patterns result from slip dislocations in the three {111} planes intersecting the (211) growth surface. The cross-hatch step height is 4 ± 1 A (limited data set). This indicates that only a bi-layer slip (Hg/Cd + Te) in the {111} slip plane occurs. For the deposition of MBE (211)B HgCdTe/CdTe/Si, the reorientation of multiple nano-ripples coalesced into “packets” forms cross-hatch patterns. The as-grown MBE (211)B CdTe/Si surface is highly variable but displays nano-ripples and no cross-hatch pattern. Three types of defects were observed by atomic force microscopy (AFM): needle, void/hillock, and voids.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
23
References
14
Citations
NaN
KQI