Photoluminescence Spectrum of NH4Br:TI after First‐Order Crystallographic Phase Transformation

Fluorescence spectra and excitation spectra of ammonium bromide activated by thallium (0.14 mol%) are investigated at various temperatures in order to determine the spectral change due to the phase transformation. It is observed that the visible emission bands disappear and the ultraviolet emission band shifts from 390 to 365 nm whereas its corresponding A absorption band shifts from 258 to 262 nm, when the NH4Br:TI undergoes first-order crystallographic phase transformation. The ultraviolet fluorescence band is composite and can be resolved into two components peaking at 314 and 365 nm. These two emission bands are attributed to AT and AX emission, similar to these reported for KBr:TI and RbBr:TI. Die Fluoreszenzspektren und die Anregungsspektren von Thallium-aktiviertem (0,14 Mol%) Ammoniumbromid werden bei verschiedenen Temperaturen untersucht, um die spektralen Anderungen infolge des Phasenubergangs zu bestimmen. Es wird beobachtet, das die Emissionsbanden im sichtbaren Bereich verschwinden und die UV-Emissionsbanden sich von 390 zu 365 nm verschieben, wahrend ihre entsprechende A-Absorptionsbande sich von 258 zu 262 nm verschiebt, wenn das NH4Br:TI einen kristallographischen Phasenubergang erster Ordnung durchlauft. Die UV-Fluoreszenzbande ist zusammengesetzt und last sich in zwei Komponenten mit Maxima bei 314 und 365 nm zerlegen. Diese beiden Emissionsbanden werden der AT- und AX-Emission, ahnlich wie fur KBr:TI und RbBr:TI berichtet, zugeordnet.