A single-phase white light emitting Pr3+ doped Ba2CaWO6 phosphor: synthesis, photoluminescence and optical properties
2018
Abstract Pr 3+ doped Ba 2 CaWO 6 phosphor were prepared by traditional high-temperature solid-state reaction technique. The structure evolution was systematically investigated by X-ray diffraction (XRD), energy–dispersive X-ray spectroscopy (EDS), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analysis. The X-ray powder diffraction patterns indicate that the prepared phosphors crystallized in the cubic double-perovskite structure. The functional groups were identified using FTIR spectra and the elements present in the composition were confirmed by the EDS profile. The morphology of the phosphor was identified using SEM and TEM analysis. The PL spectra illustrated that these phosphors could be efficiently excited by charge transfer band of host and the maximum luminescence intensity was observed at 0.06 wt% of Pr 3+ ion. Upon the charge transfer band excitation, emission spectra showed peaks at 489, 532, 647, 685 and 737 nm corresponding to 3 P 0 → 3 H 4 , 3 P 1 → 3 H 5 , 3 P 0 → 3 F 2 , 3 P 0 → 3 F 3 and 3 P 0 → 3 F 4 transitions respectively. The concentration quenching of Ba 2 CaWO 6 :Pr 3+ phosphor can be mainly attributed to dipole-dipole interaction. The CIE coordinates were estimated to be close to the white region. The decay curves are well fitted with double exponential decay models. The standard and modified Judd-Ofelt (JO) theories were used to determine the Judd-Ofelt intensity parameters, radiative transition probabilities and branching ratios. The optical properties indicate that Ba 2 CaWO 6 :Pr 3+ phosphors can produce white light emission from a single phase host and its potential application for solid-state lighting and display devices.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
54
References
18
Citations
NaN
KQI