Noise Characteristics of ZnO-Nanowire Photodetectors Prepared on ZnO:Ga/Glass Templates

In this paper, we report the fabrication of vertically well-aligned ZnO nanowire ultraviolet (UV) photodetectors on ZnO:Ga/glass templates. With 1 V applied bias, it was found that dark current density of the device was only 1.37times10 -7 A/cm 2 . It was also found that UV-to-visible rejection ratio of the fabricated photodetector was around 1000 with a maximum quantum efficiency of 12.6%. It was also found that noise equivalent power and normalized detectivity of the ZnO nanowire photodetector were 5.73times10 -11 W and 6.17times10 9 cmHz 0.5 W -1 , respectively.