High resolution electron microscopy studies of Ba4Nb14O23

The new compound, Ba4Nb14O23, has been prepared by heating mixtures of Ba5Nb4O15, Nb2O5 and Nb at 1 450°C under Ar. Ba4Nb14O23 has been studied by means of high resolution electron microscopy and X-ray powder diffraction techniques. It has a C-centered orthorhombic unit cell with a=20.782(4), b=12.448(3), c=4.148(1) A and Z=2. The structure of Ba4Nb14O23 can be considered as being an intergrowth between BaNbO3 and NbO. Characteristic building units are triple chains of corner sharing Nb6 octahedra which are connected via columns of the perovskite type structure to a three dimensional network. Untersuchungen an Ba4Nb14O23 mittels hochauflosender Elektronenmikroskopie. Die neue Verbindung Ba4Nb14O23, wurde durch Tempern von Gemengen von Ba5Nb4O15, Nb2O5 und Nb bei 1 450°C unter Ar erhalten. Ba4Nb14O23 wurde durch Untersuchungen mittels hochauflosender Elektronenmikroskopie und Rontgenpulveruntersuchungen charakterisiert. Die Verbindung kristallisiert orthorhombisch C-zentriert mit a=20.782(4), b=12.448(3), c=4.147(1) A und Z=2. Die Kristallstruktur von Ba4Nb14O23 kann als intergrowth zwischen BaNbO3 und NbO beschrieben werden. Charakteristische Baueinheiten sind Dreierketten spitzenverknupfter Nb6-Oktaeder, die uber Strange perowskitartiger Baugruppen zu einem dreidimensionalen Netzwerk verknupt sind.