Effect of strain rate on tensile mechanical properties of high-purity niobium single crystals for SRF applications

Abstract An investigation of the mechanical properties of high-purity niobium single crystals is presented. Specimens were cut with different crystallographic orientations from a large grain niobium disk and uniaxial tensile tests were conducted at strain rates between 10-4 and 103 s-1. The logarithmic strain rate sensitivity for crystals oriented close to the center of a tensile axis inverse pole figure (IPF) is ∼0.14 for all strain rates. The strain at failure (ranging from 0.4 to 0.9) is very sensitive to crystal orientation and maximal at ∼10-2 s-1 for crystals oriented close to the center of an IPF. The high anisotropy observed at quasi-static strain rates decreased with increasing strain rate. The activation of multiple slip systems in the dynamic tests could account for this reduction in anisotropy. A transition from strain hardening to softening in the plastic domain was observed at strain rates greater than approximately 6 × 10-2 s-1 for crystals oriented close to the center of a tensile axis IPF. Shear bands were observed in specimens with orientations having similarly high Schmid factors on both { 110 } and { 112 } slip families, and they are correlated with reduced ductility. Crystal rotations at fracture are compared for the different orientations using scanning electron microscopy images and EBSD orientation maps. A rotation toward the terminal stable [101] orientation was measured for the majority of specimens (with tensile axes more than ∼17° from the [001] direction) at strain rates between 1.28 × 10-2 and 1000 s-1.