Blister formation on tungsten damaged by high energy particle irradiation

Abstract In order to investigate the effect of radiation damage on hydrogen behavior in tungsten, tungsten samples with radiation damage of up to 3.5 dpa were irradiated by a mixed hydrogen–carbon ion beam. The radiation damage was produced with 700 keV negative hydrogen ion beam irradiation. The number density of blisters produced by the mixed ion beam irradiation decreased with increasing radiation damage. This was especially observed for blisters with diameters of 20 μm or less. This result showed that radiation damage produced by high-energy particle irradiation suppresses blister formation on tungsten surfaces.