Effect of γ‐irradiation on chlorendic acid based unsaturated polyesters

The effect of gamma ray irradiation on chlorendic acid based unsaturated polyesters was studied. Four different types of unsaturated polyesters, made by varying the molar ratios of chlorendic acid to isophthalie acid were irradiated with a Co60 qource. After irradiation, the chlorine content decreases rapidly as the isophthalate content in the polyester chain increases. As the chlorendle acid content increases, the change in acid value after irradiation decreases. The increase in intrinsic viscosity is quite marked in high isophthalate containing polyesters after gamma ray irradiation and there is a noticeable decrease in intrinsic viscosity after gamma irradiation of high chlorendic acid containing polyesters. The effect of gamma irradiation on the percentage of cis and trans forms of these polyesters was studied with the help of infrared spectra. It appears that as the chlorendic acid content increases, on gamma irradiation conversion from trans unsaturation to cis unsaturation increases rapidly. Der Einflus von γ-Strahlen auf Hexachlorendomethylenhexahydrophthalsaure (HCPS) enthaltende ungesattigte Polyester wurde untersucht. Dazu wurden vier Polyester mit verschiedenem Molverhaltnis an Chlorendic-Saure zu Isophthalsaure mit einer Co60-Quelle bestrahlt. Durch die Bestrahlung erniedrigt sich der Chlorgehalt stark mit zunehmendem Gehalt an Isophthalsaure. Mit steigendem Gehalt an HCPS nimmt die durch die Bestrahlung hervorgerufene Anderung der Saurezahl ab. Die Grenzviskositat steigt bei Polyestern, die viel Isophthalat-Gruppen enthalten, und falt bei solchen mit hohem Gehalt an HCPS. Der Einflus der γ-Be-strachlung auf das Verhatnis von cis- und trans-Form in diesen Polyestern wurde an Infrarotspektren untersucht. Es zeigt sich, das mit zunehmendem Gehalt an HCPS die durch die Bestrahlung verursachte trans-cis-Umwandlung stark ansteigt.