INFLUENCE DU TRAITEMENT THERMIQUE SUR LES CARACTERISTIQUES MICROFRACTOGRAPHIQUES D'UN ALLIAGE AL-MG-SI - RELATION AVEC LE COMPORTEMENT A LA CORROSION ET A LA FATIGUE

ON ETUDIE LES CARACTERISTIQUES MICROFRACTOGRAPHIQUES DES SURFACES DE FRACTURE QUE PRESENTENT LES EPROUVETTES D'UN ALLIAGE AL-MG-SI SOUMISES A DES ESSAIS DE TRACTION A DIFFERENTS STADES DU TRAITEMENT, ET ON RECHERCHE LA RELATION EXISTANT ENTRE LE TRAITEMENT THERMIQUE APPLIQUE ET LA TENDANCE A LA RUPTURE INTERCRISTALLINE. PARALLELEMENT, ON PROCEDE A UNE ETUDE SUR EPROUVETTES TESTEES A LA FATIGUE, BRISEES A DIFFERENTS NIVEAUX D'EFFORTS APPLIQUES,ON RECHERCHE L'INFLUENCE POSSIBLE DE LA TENDANCE A L'INTERCRISTALLINITE SUR LES CARACTERISTIQUES MICROGRAPHIQUES DES EPROUVETTES BRISEES A LA FATIGUE. ON A ETABLI UNE RELATION ENTRE LA TENDANCE A L'INTERCRISTALLINITE DANS LA RUPTURE A LA TRACTION ET LA SUSCEPTIBILITE DU MATERIAU A LA TENSO-CORROSION ; COMPTE-TENU EGALEMENT DES CARACTERISTIQUES FRACTOGRAPHIQUES DES EPROUVETTES DE TRACTION, ON DEDUIT LES TRAITEMENTS DE MATURATION LES PLUS CONVENABLES PERMETTANT D'EVITER D'EVENTUELS PROBLEMES DE CORROSION SOUS TENSION, SANS ALTERER LES CARACTERISTIQUES STATIQUES NI LA RESISTANCE A LA FATIGUE.