The Kinetics of the Magnetically Induced Anisotropy in Amorphous Ferromagnetic Co71Fe1Mo1Mn4Si14B9 and Fe41Ni41B18 Alloys

Analysing the kinetics of the induced anisotropy at various annealing temperatures (200, 230, 240, 260, 300, and 320 °C) it is possible to determine the spectrum of activation enthalpies for reversible processes in a nearly nonmagnetostrictive amorphous Co71Fe1Mo1Mn4Si14B9 alloy. A magnetostrictive amorphous Fe41Ni41B18 alloy is preannealed by means of a short current pulse (0.5 s, 240 °C) while applying a tensile stress in order to induce internal stresses with a well-defined stress axis. After this treatment it is possible to measure the kinetics of the uniaxial anisotropy induced by a magnetic field perpendicular to the internal stresses at a temperature Ta = 250 °C. The formation of an induced anisotropy is attributed to the thermally activated alignment of mobile atom pairs. The thermodynamic and micromagnetic properties of these atom pairs are discussed on the basis of the model of two-level-systems [1 to 3]. Fur eine nahezu magnetostriktionsfreie amorphe Co71Fe1Mo1Mn4Si14B9 Legierung wird aus der Kinetik der induzierten Anisotropie bei verschiedenen Anlastemperaturen (200, 230, 240, 260, 300 und 320 °C) das Spektrum der Aktivierungsenthalpien fur reversible Prozesse bestimmt. Eine magnetostiktive amorphe Fe41Ni41B18-Legierung wird bei angelegter Zugspannung durch einen elektrischen Strompuls (0,5 s; 240 °C) kurz getempert, um innere Spannungen mit einer definierten Richtung zu induzieren. Nach dieser Vorbehandlung ist es moglich die Kinetik der uniaxialen Anisotropie, induziert durch ein Magnetfeid senkrecht zu den inneren Spannungen bei einer Anlastemperatur Ta = 250 °C zu messen. Die Ausbildung der induzierten Anisotropie wird einer thermisch aktivierten Ausrichtung von beweglichen Atompaaren zugeschrieben und im Rahmen eines Zwei-Niveau-Modells behandelt [1 bis 3].