Diametral strength testing of hydroxyapatites doped with yttrium and fluoride
2010
Abstract Abstract This study aimed to investigate the diametral strength testing of hydroxyapatite (HA) doped with Y and fluoride with different compositions. Hydroxyapatites were synthesised by precipitation method and sintered at 900, 1100 and 1300°C for 1 h. High amounts of doping caused a decrease in relative densities of HAs. Higher sintering temperatures helped in increasing the relative densities. No second phases were observed by X-ray diffraction spectra of 2·5 mol.-%Y and 2·5 mol.-%F doped HA after the sintering at all temperatures. Trace amounts of β-tricalcium phosphate was found in 7·5 mol.-%Y and 2·5 mol.-%F doped HA sintered at 1100 and 1300°C. Diametral strength of doped HAs mostly enhanced with the addition of Y3+ and F−. 2·5YFHA sintered at 1300°C had the highest diametral strength of 11·6 MPa with a relative density of 94·3% of theoretical density.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
47
References
6
Citations
NaN
KQI