Spark plasma sintering of MgB2 in the two-temperature route
2012
Abstract Superconducting bulks of MgB 2 were obtained by an ex-situ two-temperature route applied to spark plasma sintering (SPS). Processing of samples was performed at lower temperatures than previously reported. Samples produced by the two-temperature route show a higher morphological uniformity, a higher density (above 98%), a higher Vickers hardness, and undesirable stronger microscale flux jumps, as indicated by magnetic relaxation measurements when compared to a sample obtained by the one-temperature route (95.3% relative density). At the same time, all sintered samples show approximately constant crystallite size, critical current density, irreversibility field, critical temperature, weight fraction of impurity phases (MgB 4 and MgO), and the amount of carbon accidentally introduced during SPS processing.